Electrochemical Corrosion of Oxidized Gamma TitaniumAluminide in Ringer's Solution Electrochemical corrosion of oxidized gamma titanium aluminide
Iranian Journal of Pharmaceutical Sciences,
Vol. 5 Núm. 1 (2009),
15 January 2009
,
Página 51-54
https://doi.org/10.22037/ijps.v5.41186
Resumen
Ɣ-TiAl intermetallic alloy have a good potential for use as biomaterial, due to its good corrosion resistance. In this paper, two fundamental electrochemical techniques namely electrochemical impedance spectroscopy and potentiodynamic anodic polarization were used to evaluate the corrosion performance of Ɣ-TiAl in Ringer's solution. Surface modification treatments were employed with the purpose of improving corrosion resistance. The samples were oxidized at 550 °C in air for 1h. The results show that oxidized Ti-47Al-2Cr has much better corrosion resistant in Ringer’s solution. The presence of the oxide layer formed with the surface treatments increased their corrosion resistance. The low values of corrosion rate, and the high values for corrosion potential (Ecorr) and polarization resistance (Rp)obtained experimentally implies that Ɣ-TiAl can be competitively considered as analternative metallic biomaterial.
- EIS technique
- Polarization
- Ringer's solution
- Ɣ-Titanium aluminaide
Cómo citar
Citas
[2]Kim YW, Dimiduk DM. Progress in the understanding of gamma titanium aluminides.JOM1991; 43: 40-7.
[3]Delgado-Alvarado C, Sundaram PA. Corrosion evaluation of Ti-48Al-2Cr-2Nb (at.%) in Ringer's solution. Acta Biomaterialia2006; 2: 701-8.
[4]Solar RI, Pollack SR, Korostoff E. In vitro corrosion testing of titanium surgical implant alloy: An approach to understand titanium release from implants. J Biomed Mater Res1979; 13:213-7.
[5]Mimura H, Miyagawa Y. Electrochemical corrosion behavior of titanium casting. Part I.Effects of degree of surface polishing and kind of solution. Jpn J Dent Mater1996; 15: 282-95.
[6]Semlitsch MF, Weber H, Streicher RM. Joint replacement components made of hot-forged and surface-treated Ti-6Al-7Nb alloy. Biomaterials 1992; 13: 781-8.
[7]Lopez MF, Gutierrez A, Jiménez JA. In vitro corrosion behavior of titanium alloys without vanadium. Electrochim Acta2002; 47: 1359-64.
- Resumen ##plugins.themes.ojsPlusA.frontend.article.viewed##: 72 ##plugins.themes.ojsPlusA.frontend.article.times##
- IJPS_Volume 5_Issue 1_Pages 51-54 (English) ##plugins.themes.ojsPlusA.frontend.article.downloaded##: 17 ##plugins.themes.ojsPlusA.frontend.article.times##